Hydroxyapatite
Bioceramic for porous scaffolds, bone-implant research and medical models.
HAP
Material grades
Published performance data
Values are reproduced from KUNWU technical data and depend on test method, printing, debinding and sintering conditions. Technical confirmation is required before batch design.
| ADT-HAP-HO01-B | |
|---|---|
| Powder purity | ≥96% |
| Solid loading | 36 vol% / 61 wt% |
| Viscosity at 50 s⁻¹ | 5.6 Pa·s |
| Slurry density | 1.85 g/cm³ |
| Sintering temperature | 1300°C |
| Actual density | 2.90 g/cm³ |
| Relative density | 91.8% |
| Porosity | 8.2% |
| Three-point flexural strength | 122.75 MPa |
| Compressive strength | 55.2 MPa |
| Maximum service temperature | 1100°C |